TOPAS® 9903D-10

About
Product Description TOPAS 9903D-10 is a very low glass transition temperature (T g =33°C) film extrusion grade. It is designed to deliver high shrinkage at low temperatures in shrink packaging applications. It is a moderate clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in monolayer products, and alone or in blends in multilayer films. It can be used in both cast and blown film processes. The leading film applications are shrink films and labels. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended. Due to the low glass transition temperature of this grade, shipment and storage of pellets at room temperature or below is strongly recommended. Selected Applications Shrink films and labels Food packaging Food contact Leading Attributes High shrink at low temperatures, low stress, toughness Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance Related Grades for Packaging and Film Extrusion TOPAS 9506F-500 – robust low temperature (T g =65°C) extrusion grade&&

About

Product Description TOPAS 9903D-10 is a very low glass transition temperature (T g =33°C) film extrusion grade. It is designed to deliver high shrinkage at low temperatures in shrink packaging applications. It is a moderate clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in monolayer products, and alone or in blends in multilayer films. It can be used in both cast and blown film processes. The leading film applications are shrink films and labels. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended. Due to the low glass transition temperature of this grade, shipment and storage of pellets at room temperature or below is strongly recommended. Selected Applications Shrink films and labels Food packaging Food contact Leading Attributes High shrink at low temperatures, low stress, toughness Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance Related Grades for Packaging and Film Extrusion TOPAS 9506F-500 – robust low temperature (T g =65°C) extrusion grade&&

Product Description
Supplier	Polyplastics
Generic	COC
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,High purity,Halogen free,Food contact compliance,Moisture resistance,No BPA,Copolymer,Solvent resistance,High shrinkage,Amorphous
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.02	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	0.90	g/10min	ISO 1133
230℃，2.16kg	3.7	g/10min	ISO 1133
260℃，2.16kg	7.4	g/10min	ISO 1133
Melt Volume Rate			ISO 1133
190℃，2.16 kg	1.00	cm³/10min	ISO 1133
230℃，2.16 kg	4.00	cm³/10min	ISO 1133
260℃，2.16 kg	8.00	cm³/10min	ISO 1133
Water absorption rate
Saturation, 23 ℃	0.010	%	ISO 62

film	Nominal value	Unit	Test method
film thickness
test	100	µm
Tensile modulus
100 µ m, cast thin film	1260	MPa	ISO 527-3/1
tensile strength			ISO 527-3/50
MD, fracture, 100 µ m, blow molded film	25.0	MPa	ISO 527-3/50
TD, fracture, 100 µ m, blow molded film	22.0	MPa	ISO 527-3/50
Tensile strain			ISO 527-3/50
MD, fracture, 100 µ m, cast thin film	> 150	%	ISO 527-3/50
TD, fracture, 100 µ m, cast thin film	> 100	%	ISO 527-3/50
Oxygen permeability
23 ℃, 100 µ m, extruded film, 50% RH	39	cm³·mm/m²/atm/24 hr	ASTM D3985
Water vapor transmittance
100 µ m, 23 ℃, cast film, 85% RH	0.19	g·mm/m²/atm/24 hr	ASTM F1249

THERMAL	Nominal value	Unit	Test method
Glass transition temperature	33.0	℃	ISO 11357-2

optical performance	Nominal value	Unit	Test method
gloss
60 °, 100 µ m, cast thin film	> 100		ISO 2813
Haze
100 µ m, cast thin film	< 1.0	%	ISO 14782

Process Conditions
Extrusion	Nominal value	Unit	Test method
Extruder feed section	20 to 60	°C
Barrel 1 zone temperature	210 to 220	°C
Barrel 2 zone temperature	230 to 240	°C
Barrel 3 zone temperature	230 to 240	°C
Barrel 4 zone temperature	230 to 240	°C
Nozzle temperature	230 to 240	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.