| About |
|---|
| Product Description | |
|---|---|
| Supplier | Toray |
| Material Status | Commercial: Active |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| 23℃ | 1.82 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD：3.00 mm | 0.63 | % | Internal Method |
| MD：3.00 mm | 0.13 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.020 | % | ISO 62 |
| Spiral flow | 120 | mm | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile stress | |||
| 23℃ | 160 | MPa | ISO 527-2 |
| Tensile strain | |||
| 23 ℃, fracture | 1.5 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 18000 | MPa | ISO 178 |
| Bending stress | |||
| 23℃ | 240 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 9.0 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | ＞260 | ℃ | ISO 75-2 |
| Melting temperature | 278 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 2.0E-5 | /℃ | ISO 11359-2 |
| TD | 3.1E-5 | /℃ | ISO 11359-2 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | 21 | kV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.3 mm，BK | V–0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Melt Temperature | 320 | ℃ | |
| Injection pressure | 980 | bar | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |