| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PAI |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good Electrical Properties,Ductility,Flame Characteristics,High Heat Resistance,Fatigue resistance,Good wear resistance,Solvent resistance,Low temperature toughness |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.42 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.6-0.85 | % | ASTM D995 |
| Water absorption rate | |||
| 23℃，24hr | 0.33 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 152 | MPa | ASTM D638 | |
| 192 | MPa | ASTM D1708 | |
| Tensile strain | |||
| fracture | 7.6 | % | ASTM D638 |
| fracture | 15 | % | ASTM D1708 |
| Tensile modulus | |||
| 4480 | MPa | ASTM D638 | |
| 4900 | MPa | ASTM D1708 | |
| bending strength | |||
| 23℃ | 241 | MPa | ASTM D790 |
| 232℃ | 118 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 5030 | MPa | ASTM D790 |
| 232℃ | 3590 | MPa | ASTM D790 |
| Compression modulus | 4000 | MPa | ASTM D695 |
| compressive strength | 221 | MPa | ASTM D695 |
| Poisson’s ratio | 0.45 | ASTM E132 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 2.0E+17 | Ω.cm | ASTM D257 |
| Surface resistance | 5.0E+18 | Ω.cm | ASTM D257 |
| Insulation strength | |||
| 23 | KV/mm | ASTM D149 | |
| Dielectric constant | |||
| 1 MHz | 3.90 | ASTM D150 | |
| 60 Hz | 4.20 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 0.031 | ASTM D150 | |
| 60 Hz | 0026 | ASTM D150 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 140 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 1100 | J/m | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 278 | ℃ | ASTM D648 |
| Thermal conductivity | 0.26 | W/m/K | ASTM C177 |
| Coefficient of thermal expansion | 3.1E-5 | cm/cm/°C | ASTM D696 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 180 | °C | |
| Drying time | 3.0 | Hr | |
| Moisture content | 0.05 | % | |
| Injection temperature | |||
| Temperature at the rear of the screw barrel | 300 | °C | |
| Temperature in the middle of the screw barrel | 330 | °C | |
| Front temperature of screw barrel | 360 | °C | |
| Mold head temperature | 370 | °C | |
| Mold temperature | 200-220 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |