Torlon® 4601 is a specialty wear-resistant grade of polyamide-imide (PAI). Most Torlon® PAI grades cannot be molded successfully in molds with undercuts. Torlon® 4601 has been formulated to be moldable in tools with minor undercuts and give very good performance in lubricated wear applications. Torlon® PAI has the highest strength and stiffness of any thermoplastic up to 275°C (525°F). It has outstanding resistance to wear, creep, and chemicals. Potential applications for Torlon® 4601 polyamide-imide include ball bearing cages and other molded articles that require undercut tooling.&&

About

Torlon® 4601 is a specialty wear-resistant grade of polyamide-imide (PAI). Most Torlon® PAI grades cannot be molded successfully in molds with undercuts. Torlon® 4601 has been formulated to be moldable in tools with minor undercuts and give very good performance in lubricated wear applications. Torlon® PAI has the highest strength and stiffness of any thermoplastic up to 275°C (525°F). It has outstanding resistance to wear, creep, and chemicals. Potential applications for Torlon® 4601 polyamide-imide include ball bearing cages and other molded articles that require undercut tooling.&&

Product Description
Supplier	Solvay
Generic	PAI
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,Flame Characteristics,High Heat Resistance,Good wear resistance,Solvent resistance
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.39	g/cm³	ASTM D792

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	4210	MPa	ASTM D638
tensile strength	121	MPa	ASTM D638
Tensile strain
fracture	4.1	%	ASTM D638
Bending modulus	4480	MPa	ASTM D790
bending strength	182	MPa	ASTM D790
shear strength	108	MPa	ASTM D732

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	230	J/m	ASTM D256
Notched impact strength of cantilever beam	370	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	284	℃	ASTM D648

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	177	°C
Drying time	3.0	hr
Recommended maximum moisture content	0.050	%
Barrel rear temperature	304	°C
Nozzle temperature	371	°C
Mold temperature	199 to 216	°C
Back pressure	6.89	MPa
Screw speed	50 to 100	rpm
Screw length to diameter ratio	18.0:1.0 to 24.0:1.0

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.