| About |
|---|
| PA66 33% glass fiber reinforced injection moulding grade. Heat stabilized, hydrolysis resistance. Black colour. Suitable for parts requiring high stiffness and good mechanical resistance.&& |
| Product Description | |
|---|---|
| Supplier | INVISTA |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Hydrolysis stability,Good stripping performance,Good Tensile Strength,Heat Stabilized |
| Availabilitys | North America,Latin America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD：2.0 mm | 0.90 | % | ISO 294-4 |
| MD：2.0 mm | 0.30 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，50% RH | 1.80 | % | ISO 62 |
| 23℃，24hr | 1.20 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 205 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.1 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 10500 | MPa | ISO 527-2 |
| bending strength | |||
| 23℃ | 285 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 9500 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 248 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed | 255 | ℃ | ISO 75-2/Bf |
| Melting temperature | 262 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+6 | Ω.cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| All color | 3.00mm | HB | UL-94 |
| All color | 1.50mm | HB | UL-94 |
| All color | 0.40mm | UL-94 | |
| All color | 0.71mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 12 | kJ/m² | ISO 179/1eA |
| -40℃ | 10 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 12 | kJ/m² | ISO 180-1A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70-80 | °C | |
| Drying time | 4.0-12 | Hr | |
| Recommended moisture content | <=0.20 | % | |
| Barrel rear temperature | 250-280 | °C | |
| Barrel middle temperature | 260-290 | °C | |
| Barrel front temperature | 270-300 | °C | |
| Nozzle temperature | 270-310 | °C | |
| Mold temperature | 60-140 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |