| About |
|---|
| TORZEN Marathon™ FRU4800XHL BK01 is a flame retardant, heat stabilized black Polyamide 66 resin suitable for injection molding. It does not contain elemental bromine, phosphorus or heavy metals.&& |
| Product Description | |
|---|---|
| Supplier | INVISTA |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Halogen free,Flame Characteristics,Low to no phosphorus content,Heat Stabilized,V-0 |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：2.0 mm | 1.3 to 1.6 | % | ISO 294-4 |
| MD：2.0 mm | 1.3 to 1.6 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3900 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 73.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 13 | % | ISO 527-2 |
| bending strength | 105 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 2.8 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 85.0 | ℃ | ISO 75-2/A |
| Melting temperature | 263 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the resistance to leakage and marking index | |||
| 3.00 mm | 600 | V | UL 746 |
| Compared to the resistance to leakage and marking index | |||
| 3.00 mm | PLC 0 | ASTM D3638 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.40 mm | V-0 | UL 94 | |
| 0.80 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Flammability level | IEC 60695-11-10, -20 | ||
| 0.40 mm | V-0 | IEC 60695-11-10, -20 | |
| 0.8 mm | V-0 | IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | IEC 60695-11-10, -20 | |
| 3.0 mm | V-0 | IEC 60695-11-10, -20 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 0.40 mm | 960 | ℃ | IEC 60695-2-12 |
| 0.80 mm | 960 | ℃ | IEC 60695-2-12 |
| 1.5 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.4 mm | 990 | ℃ | IEC 60695-2-13 |
| 0.8 mm | 990 | ℃ | IEC 60695-2-13 |
| 1.5 mm | 990 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.080 to 0.18 | % | |
| Barrel rear temperature | 250 to 270 | °C | |
| Barrel middle temperature | 260 to 280 | °C | |
| Barrel front temperature | 270 to 280 | °C | |
| Nozzle temperature | 270 to 280 | °C | |
| Processing (melt) temperature | 270 to 290 | °C | |
| Mold temperature | 50 to 90 | °C | |
| Back pressure | 0.200 to 1.00 | MPa | |
| Screw speed | 75 to 180 | rpm | |
| Cushion | 4.00 to 6.00 | mm | |
| Vent depth | 7.0E-3 to 0.040 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |