| About |
|---|
| TORZEN® T2000HSL NC01 is a toughened, heat stabilized, natural, PA66 resin with good impact strength, stiffness, weld line strength, surface appearance and flow.&& |
| Product Description | |
|---|---|
| Supplier | INVISTA |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good surface appearance,High impact resistance,Good liquidity,Heat Stabilized |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.09 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：2.0 mm | 1.6 to 1.9 | % | ISO 294-4 |
| MD：2.0 mm | 1.6 to 1.9 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 60.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 30 | % | ISO 527-2 |
| yield | 4.0 | % | ISO 527-2 |
| Bending modulus | 2400 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40℃ | 12 | kJ/m² | ISO 179 |
| 23℃ | 18 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | No Break | ISO 179 | |
| 23℃ | No Break | ISO 179 | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 17 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 65.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 187 | ℃ | ISO 75-2/B |
| Melting temperature | 262 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD：23~55℃，2 mm | 1.0E-4 | 1/℃ | ISO 11359-2 |
| MD：23~55℃，2 mm | 1.0E-4 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.080 to 0.18 | % | |
| Barrel rear temperature | 250 to 270 | °C | |
| Barrel middle temperature | 270 to 290 | °C | |
| Barrel front temperature | 270 to 290 | °C | |
| Nozzle temperature | 270 to 290 | °C | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 50 to 90 | °C | |
| Back pressure | 0.200 to 1.00 | MPa | |
| Cushion | 4.00 to 6.00 | mm | |
| Vent depth | 7.0E-3 to 0.040 | mm | |
| Screw speed | Low rpm | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |