| About |
|---|
| EVA 1005 VN 2 is made by a high pressure tubular process. Grade for transparent and resistant films. Application examples : Stretch, coextrusion, frozen food, agricultural film.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Inoxidizability,Copolymer |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.925 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.50 | g/10min | ISO 1133 |
| Vinyl acetate content | 5.5 | wt% | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 160 | MPa | ISO 527-2 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 40 | µm | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 40 µ m, blow molded film | 9.50 | MPa | ISO 527-3 |
| TD, yield, 40 µ m, blow molded film | 8.50 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 40 µ m, blow molded film | 32.0 | MPa | ISO 527-3 |
| TD, fracture, 40 µ m, blow molded film | 27.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 40 µ m, blow molded film | 300 | % | ISO 527-3 |
| TD, fracture, 40 µ m, blow molded film | 570 | % | ISO 527-3 |
| Drop hammer impact | |||
| 40 µ m, blow molded film | 340 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD: 40 µ m, blow molded film | 34 | N | ISO 6383-2 |
| TD: 40 µ m, blow molded film | 33 | N | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 90.0 | ℃ | ISO 306 |
| Melting temperature | 104 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 40 µ m, blow molded film | 8.8 | % | ISO 14782 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 160 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |