| EVA 1040 VN 4 is made by a high pressure tubular process. Grade for very flexible films with high transparancy and good mechanical properties. Application examples : thin stretch film for food packaging, coextrusion, cling film.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good flexibility,Inoxidizability,Copolymer |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 0.935 | g/cm³ | ISO 1183 |
| — | 0.935 | g/cm³ | ISO 1183-1 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 4.5 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 190℃，2.16 kg | 5.00 | cm³/10min | ISO 1133 |
| Vinyl acetate content | 14.0 | wt% | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 62.0 | MPa | ISO 527-2 |
| — | 75.0 | MPa | ISO 527-2 3 |
| Tensile strain | |||
| fracture | > 50 | % | ISO 527-2 6 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 527-3 | ||
| yield | 5.00 | MPa | ISO 527-2 4 |
| MD, yield, 40 µ m, blow molded film | 6.50 | MPa | |
| TD, yield, 40 µ m, blow molded film | 4.90 | MPa | |
| MD, fracture, 40 µ m, blow molded film | 27.0 | MPa | |
| TD, fracture, 40 µ m, blow molded film | 23.0 | MPa | |
| Tensile strain | ISO 527-3 | ||
| yield | 25 | % | ISO 527-2 5 |
| MD, fracture, 40 µ m, blow molded film | 370 | % | |
| TD, fracture, 40 µ m, blow molded film | 650 | % | |
| Drop hammer impact | |||
| 40 µ m, blow molded film | 300 | g | ISO 7765-1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| — | 68.0 | ℃ | ISO 306 |
| B50 | 68.0 | ℃ | ISO 306 7 |
| Melting temperature | |||
| DSC | |||
| — | 90.0 | ℃ | ISO 3146 |
| — | 92.0 | ℃ | ISO 11357-3 9 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |