| About |
|---|
| HIGH MOLECULAR WEIGHT HDPE FILM RESIN Characteristics Good tear strength Good impact strength Good processability Excellent bubble stability Applications T-shirt sacks Trash can liners Merchandise bags Coex applications&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | HMW-HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,High molecular weight,Good tear strength,High density |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.950 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.070 | g/10min | |
| 190℃，21.6kg | 9.0 | g/10min | |
| 190℃，5.0kg | 0.31 | g/10min | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 20 | µm | |
| Secant modulus | ASTM D882A | ||
| 2% secant, MD: 20 µ m | 841 | MPa | |
| 2% secant, TD: 20 µ m | 910 | MPa | |
| tensile strength | ASTM D882A | ||
| MD, yield, 20 µ m | 36.5 | MPa | |
| TD, yield, 20 µ m | 34.5 | MPa | |
| MD, fracture, 20 µ m | 61.4 | MPa | |
| TD, fracture, 20 µ m | 58.6 | MPa | |
| Tensile strain | ASTM D882A | ||
| MD, fracture, 20 µ m | 300 to 500 | % | |
| TD, fracture, 20 µ m | 300 to 500 | % | |
| Drop hammer impact | |||
| 20 µm | 350 | g | ASTM D1709-A |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：20 µm | 24 | g | |
| TD：20 µm | 120 | g | |
| Water vapor transmittance | |||
| 38℃，20 µm | 12 | g/m²/24 hr | ASTM F1249 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 127 | ℃ | DSC |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |