| About |
|---|
| High Molecular Weight HDPE Bimodal Film Resin Characteristics Broad molecular weight distribution Excellent tear strength Exceptional impact strength Excellent processability Applications T-shirt sacks Trash can liners Merchandise bags Multi-wall liner Deli wrap&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | HMW-HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,High molecular weight,Good tear strength,High density,Bimodal molecular weight distribution |
| Availabilitys | North America |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.951 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.080 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 11 | g/10min | ASTM D1238 |
| 190℃，5.0kg | 0.32 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 20 | µm | |
| Secant modulus | |||
| 2% secant, TD, 20 µ m, blow molded film | 910 | MPa | ASTM D882A |
| 2% secant, MD, 20 µ m, blow molded film | 841 | MPa | ASTM D882A |
| tensile strength | |||
| TD, fracture, 20 µ m, blow molded film | 67.6 | MPa | ASTM D882A |
| TD, yield, 20 µ m, blow molded film | 34.5 | MPa | ASTM D882A |
| MD, fracture, 20 µ m, blow molded film | 63.4 | MPa | ASTM D882A |
| MD, yield, 20 µ m, blow molded film | 36.5 | MPa | ASTM D882A |
| Tensile strain | |||
| TD, fracture, 20 µ m, blow molded film | 300 to 500 | % | ASTM D882A |
| MD, fracture, 20 µ m, blow molded film | 300 to 500 | % | ASTM D882A |
| Drop hammer impact | |||
| 20 µ m, blow molded film | 350 | g | ASTM D1709-A |
| tear strength | |||
| TD, 20 µ m, blow molded film | 120 | g | ASTM D1922 |
| MD, 20 µ m, blow molded film | 24 | g | ASTM D1922 |
| Water vapor transmittance | |||
| 38 ℃, 20 µ m, blow molded film | 12 | g/m²/24 hr | ASTM F1249 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 132 | ℃ | ASTM D3417 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |