| About |
|---|
| Characteristics: HDPE 50100.2: Good melt strength, Excellent stress cracking resistance, good stiffness, excellent impact strength, exceptional forming characteristics. Applications: 50100.2 is recommended for sheet extrusion, thermoforming, truck bed liners, dunnage containers, large part formed articles.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | HMW-HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,High molecular weight,Good melt strength,High density,High ESCR |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.950 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，21.6kg | 9.5 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 100% non-ionic detergent, F50 | > 600 | hr | ASTM D1693B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 26.2 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 600 | % | ASTM D638 |
| Bending modulus | 1210 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 530 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 127 | ℃ | ASTM D3417 |
| Linear coefficient of thermal expansion | |||
| MD | 1.8E-4 | 1/℃ | ASTM D696 |
| Hot deformation temperature | 78 | ℃ | ASTM D648 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Temperature of hot forming mold | 154 to 182 | ℃ | ASTM F1248 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 199 to 249 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type IV, 2,0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |