| HDPE 6410: Unique combination of high stiffness and clarity, Good moisture barrier properties, good processability, good compatibility with LDPE and LLDPE Applications: Paper overwrap, cup overwrap, plate overwrap, envelope windows, release liners, stand-up bags, specialty monolayer films, coextruded films.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | MMW-HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good Clarity,Moisture resistance,High density |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.961 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 1.2 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 33 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Secant modulus | ASTM D882A | ||
| 1% secant, MD: 25 µ m, blow molded film | 862 | MPa | ASTM D882A |
| 2% secant, MD: 25 µ m, blow molded film | 689 | MPa | ASTM D882A |
| Secant modulus | ASTM D882A | ||
| 1% secant, TD: 25 µ m, blow molded film | 883 | MPa | ASTM D882A |
| 2% secant, TD: 25 µ m, blow molded film | 703 | MPa | ASTM D882A |
| tensile strength | |||
| TD, fracture, 25 µ m, blow molded film | 23.4 | MPa | ASTM D882A |
| TD, yield, 25 µ m, blow molded film | 27.6 | MPa | ASTM D882A |
| MD, fracture, 25 µ m, blow molded film | 51.7 | MPa | ASTM D882A |
| MD, yield, 25 µ m, blow molded film | 26.2 | MPa | ASTM D882A |
| Tensile strain | |||
| TD, fracture, 25 µ m, blow molded film | 700 | % | ASTM D882A |
| MD, fracture, 25 µ m, blow molded film | 700 | % | ASTM D882A |
| tear strength | |||
| TD, 25 µ m, blow molded film | 390 | g | ASTM D1922 |
| MD, 25 µ m, blow molded film | 24 | g | ASTM D1922 |
| Water vapor transmittance | |||
| 38 ℃, 25 µ m, blow molded film | 6.2 | g/m²/24 hr | ASTM F1249 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 134 | ℃ | ASTM D3417 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 25.4 µ m, blow molded film | 50 | ASTM D523 | |
| Haze | |||
| 25.4 µ m, blow molded film | 15 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |