| HDPE 9458: High stiffness, high tensile strength, good heat resistance, excellent bubble stability, good compatibility with LDPE and LLDPE. Applications: Release liners, stand-up bags, coextruded films, shipping sacks, multi-walled liners, oriented film structures, specialty packaging.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | MMW-HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Tensile Strength,High density,Heat Resistance, Good |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.958 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.45 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Secant modulus | |||
| 1% secant, TD, 25 µ m, blow molded film | 1370 | MPa | ASTM D882A |
| 1% secant, MD, 25 µ m, blow molded film | 1050 | MPa | ASTM D882A |
| tensile strength | |||
| TD, fracture, 25 µ m, blow molded film | 17.9 | MPa | ASTM D882A |
| TD, yield, 25 µ m, blow molded film | 17.9 | MPa | ASTM D882A |
| MD, fracture, 25 µ m, blow molded film | 53.1 | MPa | ASTM D882A |
| MD, yield, 25 µ m, blow molded film | 31.0 | MPa | ASTM D882A |
| Tensile strain | |||
| TD, fracture, 25 µ m, blow molded film | < 10 | % | ASTM D882A |
| MD, fracture, 25 µ m, blow molded film | 270 | % | ASTM D882A |
| Drop hammer impact | |||
| 25 µ m, blow molded film | < 50 | g | ASTM D1709-A |
| tear strength | |||
| TD, 25 µ m, blow molded film | 1100 | g | ASTM D1922 |
| MD, 25 µ m, blow molded film | 15 | g | ASTM D1922 |
| Water vapor transmittance | |||
| 38 ℃, 25 µ m, blow molded film | 11 | g/m²/24 hr | ASTM F1249 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 193 to 216 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 1.0 in/min |
| 3. 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |