| About |
|---|
| HDPE D4720: Excellent processability, good tear and impact strength, good stiffness, excellent compatibility with LDPE and LLDPE, excellent drawdown, good moisture barrier properties. Applications: Multi-wall liner, gas flush poultry bags, mailing envelopes, heavy-duty shipping sacks, fresh cut produce packaging, coextrusions.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | MMW-HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,High impact resistance,Good dissection,Moisture resistance,Good tear strength,High density |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.947 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.28 | g/10min | |
| 190℃，21.6kg | 20 | g/10min | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Secant modulus | ASTM D882A | ||
| 1% secant, MD: 25 µ m | 710 | MPa | |
| 1% secant, TD: 25 µ m | 1000 | MPa | |
| tensile strength | ASTM D882A | ||
| MD, yield, 25 µ m | 24.1 | MPa | |
| MD, yield, 25 µ m | 23.4 | MPa | |
| TD, yield, 25 µ m | 25.5 | MPa | |
| TD, yield, 25 µ m | 26.2 | MPa | |
| MD, fracture, 25 µ m | 4.83 | MPa | |
| MD, fracture, 25 µ m | 62.1 | MPa | |
| TD, fracture, 25 µ m | 39.3 | MPa | |
| TD, fracture, 25 µ m | 18.6 | MPa | |
| Tensile strain | ASTM D882A | ||
| MD, fracture, 25 µ m | 600 | % | |
| MD, fracture, 25 µ m | 450 | % | |
| TD, fracture, 25 µ m | 700 | % | |
| TD, fracture, 25 µ m | 600 | % | |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：25 µm | 28 | g | |
| MD：25 µm | 10 | g | |
| TD：25 µm | 530 | g | |
| TD：25 µm | 1500 | g | |
| Water vapor transmittance | |||
| 38℃，25 µm | 7.8 | g/m²/24 hr | ASTM E96 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 131 | ℃ | ASTM D3417 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Drop hammer impact | ASTM D1709 | ||
| 25.4 µm | 100 | g | |
| 25.4 µm | g |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 193 to 216 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. High Stalk Extrusion |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |