| LDPE 1700 MN 18 C is a low density polyethylene made by a high pressure autoclave process. Grade for easy flow injection moulding of flexible parts, powder production for grinding and master-batches.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good liquidity,Low density |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 70 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 50 | ISO 868 | |
| Tensile modulus | 150 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 7.00 | MPa | ISO 527-2 |
| yield | 8.00 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 120 | % | ISO 527-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 84.0 | ℃ | ISO 306 |
| Melting temperature | 105 | ℃ | ISO 11357-3 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 160 to 220 | °C | |
| Mold temperature | 30 to 40 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |