TOTAL Polyethylene Lumicene® M 2735

About
Lumicene® mPE M 2735 is a Lumicene® metallocene based Polyethylene with hexene as comonomer. Lumicene® mPE M 2735 can be processed at high output rates with low extrusion pressure, low neck-in, excellent drawability and good gauge control. Together with these features, Lumicene® M 2735 ensures films with outstanding optical properties and excellent impact and tear resistance. Lumicene® mPE M 2735 is suited for many applications in the field of cast film, stretch wrap film (low cling), hygiene film (f.e. diaper backsheet), lamination and artificial grass.&&

About

Lumicene® mPE M 2735 is a Lumicene® metallocene based Polyethylene with hexene as comonomer. Lumicene® mPE M 2735 can be processed at high output rates with low extrusion pressure, low neck-in, excellent drawability and good gauge control. Together with these features, Lumicene® M 2735 ensures films with outstanding optical properties and excellent impact and tear resistance. Lumicene® mPE M 2735 is suited for many applications in the field of cast film, stretch wrap film (low cling), hygiene film (f.e. diaper backsheet), lamination and artificial grass.&&

Product Description
Supplier	TOTAL
Generic	MDPE
Material Status	Commercial: Active
Features	High impact resistance,Good dissection,Optical performance,Good Gauge Control,Low shrinkage,Inoxidizability,Good tear strength,Hexene copolymers
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.927	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	3.5	g/10min	ISO 1133

film	Nominal value	Unit	Test method
film thickness
test	20	µm
tensile strength			ISO 527-3
MD, yield, 20 µ m, blow molded film	9.00	MPa	ISO 527-3
TD, yield, 20 µ m, blow molded film	9.00	MPa	ISO 527-3
tensile strength			ISO 527-3
MD, fracture, 20 µ m, blow molded film	39.0	MPa	ISO 527-3
TD, fracture, 20 µ m, blow molded film	24.0	MPa	ISO 527-3
Tensile strain			ISO 527-3
MD, fracture, 20 µ m, extruded film	470	%	ISO 527-3
TD, fracture, 20 µ m, extruded film	530	%	ISO 527-3
Drop hammer impact
20 µ m, cast thin film	100	g	ISO 7765-1
Elmandorf tear strength			ISO 6383-2
MD: 20 µ m, cast thin film	50	N	ISO 6383-2
TD: 20 µ m, cast thin film	120	N	ISO 6383-2

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	118	℃	ISO 306
Melting temperature	119	℃	ISO 11357-3

optical performance	Nominal value	Unit	Test method
gloss
45 °, 20 µ m, cast thin film	89		ASTM D2457
Haze
20.0 µ m, cast thin film	1.3	%	ISO 14782

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	240 to 280	°C
Traction roller	20 to 60	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.