| About |
|---|
| Lumicene® mPE M 3410 EP is a second generation metallocene based Medium Density Polyethylene with hexene as comonomer. Lumicene® mPE M 3410 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The combination of these features brings a significant downgauging potential. Lumicene® mPE M 3410 EP is especially dedicated to film applications where high gloss and high transparency are required, particularly in blend and in coextrusion with LLDPE or LDPE. Lumicene® mPE M 3410 EP is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as collation shrink, mailing film, heavy-duty sacks, bags, lamination and hygiene film.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | MDPE |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good surface appearance,Good Gauge Control,Inoxidizability,Hexene copolymers |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.934 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.90 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 40 | µm | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 40 µ m, blow molded film | 17.0 | MPa | ISO 527-3 |
| TD, yield, 40 µ m, blow molded film | 18.0 | MPa | ISO 527-3 |
| MD, fracture, 40 µ m, blow molded film | 47.0 | MPa | ISO 527-3 |
| TD, fracture, 40 µ m, blow molded film | 43.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 40 µ m, blow molded film | 630 | % | ISO 527-3 |
| TD, fracture, 40 µ m, blow molded film | 700 | % | ISO 527-3 |
| Drop hammer impact | |||
| 40 µ m, blow molded film | 100 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD: 40 µ m, blow molded film | 20 | N | ISO 6383-2 |
| TD: 40 µ m, blow molded film | 100 | N | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 123 | ℃ | ISO 306 |
| Melting temperature | 124 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 40.0 µ m, blow molded film | 60 | ASTM D2457 | |
| Haze | |||
| 40 µ m, blow molded film | 9.0 | % | ISO 14782 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blown Film Melt Temperature | 180 to 230 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 200 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |