TOTAL Polyethylene Lumicene® M 3427

About
Lumicene® mPE M 3427 is a second generation metallocene based Polyethylene with hexene as comonomer. Lumicene® mPE M 3427 can be processed at high output rates with low extrusion pressure, low neck-in, excellent drawability and good gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The combination of these features combined with excellent optical properties brings a significant downgauging potential. Lumicene® mPE M 3427 is suited for many applications in the field of consumer, food and hygiene packaging such as hygiene film, stretch wrap (non cling layer) and lamination.&&

About

Lumicene® mPE M 3427 is a second generation metallocene based Polyethylene with hexene as comonomer. Lumicene® mPE M 3427 can be processed at high output rates with low extrusion pressure, low neck-in, excellent drawability and good gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The combination of these features combined with excellent optical properties brings a significant downgauging potential. Lumicene® mPE M 3427 is suited for many applications in the field of consumer, food and hygiene packaging such as hygiene film, stretch wrap (non cling layer) and lamination.&&

Product Description
Supplier	TOTAL
Generic	MDPE
Material Status	Commercial: Active
Features	Good dissection,Optical performance,Good Gauge Control,Low shrinkage,Inoxidizability,Hexene copolymers
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.934	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	3.1	g/10min	ISO 1133

film	Nominal value	Unit	Test method
film thickness
test	20	µm
tensile strength			ISO 527-3
MD, yield, 20 µ m, blow molded film	12.0	MPa	ISO 527-3
TD, yield, 20 µ m, blow molded film	11.5	MPa	ISO 527-3
MD, fracture, 20 µ m, blow molded film	39.0	MPa	ISO 527-3
TD, fracture, 20 µ m, blow molded film	27.0	MPa	ISO 527-3
Tensile strain			ISO 527-3
MD, fracture, 20 µ m, cast thin film	480	%	ISO 527-3
TD, fracture, 20 µ m, cast thin film	590	%	ISO 527-3
Drop hammer impact
20 µ m, cast thin film	53	g	ISO 7765-1
Elmandorf tear strength			ISO 6383-2
MD: 20 µ m, cast thin film	21	N	ISO 6383-2
TD: 20 µ m, cast thin film	120	N	ISO 6383-2

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	120	℃	ISO 306
Melting temperature	123	℃	ISO 11357-3

optical performance	Nominal value	Unit	Test method
gloss
45 °, 20 µ m, cast thin film	86		ASTM D2457
Haze
20.0 µ m, cast thin film	2.3	%	ISO 14782

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	240 to 280	°C
Traction roller	20 to 60	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.