| About |
|---|
| Lumicene® mPE M6012 EP is a metallocene High Density homopolymer Polyethylene designed to have High Water Vapour Barrier (low WVTR). Lumicene® mPE M6012 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control. The outstanding Water Vapour Barrier gives a significant down-gauging potential for some applications as dry food packaging.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Gauge Control,Moisture resistance,Inoxidizability,High density,Homopolymer |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.2 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 40 | µm | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 40 µ m, blow molded film | 27.5 | MPa | ISO 527-3 |
| TD, yield, 40 µ m, blow molded film | 31.5 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 40 µ m, blow molded film | 52.5 | MPa | ISO 527-3 |
| TD, fracture, 40 µ m, blow molded film | 52.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 40 µ m, blow molded film | 870 | % | ISO 527-3 |
| TD, fracture, 40 µ m, blow molded film | 1000 | % | ISO 527-3 |
| Drop hammer impact | |||
| 40 µ m, blow molded film | 55 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD: 40 µ m, blow molded film | 8.0 | N | ISO 6383-2 |
| TD: 40 µ m, blow molded film | 28 | N | ISO 6383-2 |
| Water vapor permeability | 1.6 | g/m²/24 hr | ASTM E96 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 134 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 40.0 µ m, blow molded film | 54 | ASTM D2457 | |
| Haze | |||
| 40 µ m, blow molded film | 15 | % | ISO 14782 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 200 to 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Procedure E |
| 3. 35µm, 38°C, 90% RH |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |