| Lumicene® Supertough 32ST05 is a polyethylene blown film grade that is especially designed to have an excellent processability on extrusion and conversion lines and to give a very high toughness – stiffness balance allowing new innovative multilayer film concepts. Thanks to this innovative design, Lumicene® Supertough 32ST05 brings a huge down-gauging potential in the film market.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | MDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Inoxidizability,Rigid-tough balance |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.931 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.50 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 40 | µm | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 40 µ m, blow molded film | 15.0 | MPa | ISO 527-3 |
| MD, yield, 40 µ m, blow molded film | 15.5 | MPa | ISO 527-3 |
| TD, yield, 40 µ m, blow molded film | 15.0 | MPa | ISO 527-3 |
| TD, yield, 40 µ m, blow molded film | 16.0 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 40 µ m, blow molded film | 56.0 | MPa | ISO 527-3 |
| MD, fracture, 40 µ m, blow molded film | 57.0 | MPa | ISO 527-3 |
| TD, fracture, 40 µ m, blow molded film | 56.0 | MPa | ISO 527-3 |
| TD, fracture, 40 µ m, blow molded film | 48.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 40 µ m, blow molded film | 590 | % | ISO 527-3 |
| MD, fracture, 40 µ m, blow molded film | 580 | % | ISO 527-3 |
| TD, fracture, 40 µ m, blow molded film | 590 | % | ISO 527-3 |
| TD, fracture, 40 µ m, blow molded film | 630 | % | ISO 527-3 |
| Drop hammer impact | ISO 7765-1 | ||
| 40 µ m, blow molded film | 280 | g | ISO 7765-1 |
| 40 µ m, blow molded film | 340 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD: 40 µ m, blow molded film | 72 | N | ISO 6383-2 |
| MD: 40 µ m, blow molded film | 55 | N | ISO 6383-2 |
| TD: 40 µ m, blow molded film | 150 | N | ISO 6383-2 |
| TD: 40 µ m, blow molded film | 200 | N | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 115 | ℃ | ISO 306 |
| Melting temperature | 123 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | ASTM D2457 | ||
| 45 °, 40.0 µ m, blow molded film | 38 | ASTM D2457 | |
| 45 °, 40.0 µ m, blow molded film | 50 | ASTM D2457 | |
| Haze | ISO 14782 | ||
| 40 µ m, blow molded film | 14 | % | ISO 14782 |
| 40 µ m, blow molded film | 14 | % | ISO 14782 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 180 to 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. High Neck Configuration |
| 3. Low Neck Configuration |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |