TOTAL Polypropylene PPC 2660

About
Polypropylene PPC 2660 is heterophasic copolymer with a Melt Flow Index of 0.8 g/10 min. Polypropylene PPC 2660 is characterized by a low fluidity hence good melt strength to provide ease of processing and good manufactured article properties. Polypropylene PPC 2660 is suitable particularly for the extrusion of corrugated cardboard, blown film, sheet and pipes and for blow-moulding applications where a very high impact resistance is required.&&

About

Polypropylene PPC 2660 is heterophasic copolymer with a Melt Flow Index of 0.8 g/10 min. Polypropylene PPC 2660 is characterized by a low fluidity hence good melt strength to provide ease of processing and good manufactured article properties. Polypropylene PPC 2660 is suitable particularly for the extrusion of corrugated cardboard, blown film, sheet and pipes and for blow-moulding applications where a very high impact resistance is required.&&

Product Description
Supplier	TOTAL
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Excellent Processability,Low liquidity,High impact resistance,Good melt strength,Impact copolymer
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.905	g/cm³	ISO 1183
Apparent density	0.53	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	0.80	g/10min	ISO 1133

film	Nominal value	Unit	Test method
film thickness
test	40	µm
tensile strength
yield	24.0	MPa	ISO 527-2
MD, fracture, 40 µ m, blow molded film	80.0	MPa	ISO 527-3
MD, yield, 40 µ m, blow molded film	30.0	MPa	ISO 527-3
Tensile strain
yield	13	%	ISO 527-2
MD, fracture, 40 µ m, blow molded film	600	%	ISO 527-3
Drop hammer impact
40 µ m, blow molded film	100	g	ISO 7765-1
Elmandorf tear strength			ISO 6383-2
MD: 40 µ m, blow molded film	5.0	N	ISO 6383-2
TD: 40 µ m, blow molded film	45	N	ISO 6383-2

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179
-20℃	6.0	kJ/m²	ISO 179
23℃	> 50	kJ/m²	ISO 179
Impact strength of cantilever beam notch			ISO 180
-20℃	6.0	kJ/m²	ISO 180
23℃	> 50	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	50.0	℃	ISO 75-2/A
0.45 MPa, unannealed	88.0	℃	ISO 75-2/B
Vicat Softening Temp
A50	148	℃	ISO 306/A50
B50	70.0	℃	ISO 306
Melting temperature
DSC	165	℃	ISO 3146

optical performance	Nominal value	Unit	Test method
gloss
40 µ m, blow molded film	14		ASTM D2457
Haze
40 µ m, blow molded film	41	%	ISO 14782

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	1200	MPa	ISO 527-2
Bending modulus	1100	MPa	ISO 178
Rockwell hardness
R-level	74		ISO 2039-2

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.