| Polypropylene PPC 7652 is nucleated and antistatic heterophasic copolymer with a Melt Flow Index of 16 g/10 min. Polypropylene PPC 7652 is a medium flow grade intended for a wide range of injection moulding applications including battery cases, electrical appliance housings, toys, closures and lids. Polypropylene PPC 7652 has been specially formulated to give antistatic performance.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Nucleation,Moderate liquidity,Antistatic property,Impact copolymer |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent density | 0.53 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 16 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20℃ | 6.0 | kJ/m² | ISO 179 |
| 23℃ | 10 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | ISO 180 | ||
| -20℃ | 5.5 | kJ/m² | ISO 180 |
| 23℃ | 9.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 52.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 92.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 145 | ℃ | ISO 306/A50 |
| B50 | 75.0 | ℃ | ISO 306 |
| Melting temperature | |||
| DSC | 165 | ℃ | ISO 3146 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1450 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 26.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 10 | % | ISO 527-2 |
| Bending modulus | 1350 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 85 | ISO 2039-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |