TOTAL Polypropylene PPH 3281

About
Polypropylene 3281: The high melt strength of TOTAL Polypropylene 3281 allows uniform draw down during processing, resulting in maximum line speeds and a good balance of physical properties. Process Stability: Excellent polymer stability of TOTAL 3281 produces consistent product properties during extrusion, even with the use of regrind. FDA: 3281 complies with all applicable FDA regulations and may be used under these provisions for food contact applications. Applications: 3281 is recommended for sheet and strapping applications where high melt strength and high extrusion speeds are required. Processing: 3281 resin processes on conventional extrusion equipment with typical melt temperatures of 390-450°F (200-232°C).&&

About

Polypropylene 3281: The high melt strength of TOTAL Polypropylene 3281 allows uniform draw down during processing, resulting in maximum line speeds and a good balance of physical properties. Process Stability: Excellent polymer stability of TOTAL 3281 produces consistent product properties during extrusion, even with the use of regrind. FDA: 3281 complies with all applicable FDA regulations and may be used under these provisions for food contact applications. Applications: 3281 is recommended for sheet and strapping applications where high melt strength and high extrusion speeds are required. Processing: 3281 resin processes on conventional extrusion equipment with typical melt temperatures of 390-450°F (200-232°C).&&

Product Description
Supplier	TOTAL
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Low liquidity,Food contact compliance,Good melt strength,Homopolymer
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.905	g/cm³	ASTM D1505
Melt Flow Rate
230℃，2.16kg	1.3	g/10min	ASTM D1238

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	43	J/m	ASTM D256-A
23℃	1600	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	104	℃	ASTM D648
Melting temperature	166	℃	DSC
Linear coefficient of thermal expansion
MD	1.0E-4	1/℃	ASTM D696

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	81		ASTM D1706
Tensile modulus	1520	MPa	ASTM D638
tensile strength
yield	33.8	MPa	ASTM D638
Tensile strain
fracture	8.0	%	ASTM D638
Bending modulus	1380	MPa	ASTM D790
Rockwell hardness
R-level	90		ASTM D785

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	199 to 232	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.