TOTAL Polypropylene PPH 9069

About
Polypropylene PPH 9069 is homopolymer with a Melt Flow Index of 25 g/10 min. Polypropylene PPH 9069 is intended for applications in non-wovens. It is also suitable for extrusion of bulk continuous filament (BCF) and continuous filament (CF) fibres. Polypropylene PPH 9069 has a special anti gas-fading formulation to significantly reduce yellowing in fibres. The high fluidity of polypropylene PPH 9069 also makes it especially suitable for high speed injection moulding of thin walled articles.&&

About

Polypropylene PPH 9069 is homopolymer with a Melt Flow Index of 25 g/10 min. Polypropylene PPH 9069 is intended for applications in non-wovens. It is also suitable for extrusion of bulk continuous filament (BCF) and continuous filament (CF) fibres. Polypropylene PPH 9069 has a special anti gas-fading formulation to significantly reduce yellowing in fibres. The high fluidity of polypropylene PPH 9069 also makes it especially suitable for high speed injection moulding of thin walled articles.&&

Product Description
Supplier	TOTAL
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	High liquidity,Solvent resistance,Homopolymer
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.905	g/cm³	ISO 1183
Apparent density	0.53	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	25	g/10min	ISO 1133

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	3.5	kJ/m²	ISO 179
Impact strength of cantilever beam notch
23℃	3.0	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	55.0	℃	ISO 75-2/A
0.45 MPa, unannealed	100	℃	ISO 75-2/B
Vicat Softening Temp
A50	153	℃	ISO 306/A50
B50	89.0	℃	ISO 306
Melting temperature
DSC	165	℃	ISO 3146

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	1600	MPa	ISO 527-2
tensile strength
yield	32.0	MPa	ISO 527-2
Tensile strain
yield	9.0	%	ISO 527-2
Bending modulus	1500	MPa	ISO 178
Rockwell hardness
R-level	95		ISO 2039-2

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.