| About |
|---|
| Total Polypropylene PPR 3260 is a random copolymer polypropylene with a Melt Flow Index of 1.8 g/min suitable for the manufacturing of films having easy heat weldability in the blown process.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good heat sealing,Random copolymer,Welding |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.902 | g/cm³ | ISO 1183 |
| Apparent density | 0.53 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 1.8 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 40 | µm | |
| tensile strength | |||
| yield | 26.0 | MPa | ISO 527-2 |
| MD, fracture, 40 µ m, blow molded film | 76.0 | MPa | ISO 527-3 |
| MD, yield, 40 µ m, blow molded film | 33.0 | MPa | ISO 527-3 |
| Tensile strain | |||
| yield | 10 | % | ISO 527-2 |
| MD, fracture, 40 µ m, blow molded film | 650 | % | ISO 527-3 |
| Drop hammer impact | |||
| 40 µ m, blow molded film | 36 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD: 40 µ m, blow molded film | 3.0 | N | ISO 6383-2 |
| TD: 40 µ m, blow molded film | 13 | N | ISO 6383-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 8.5 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 7.5 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 130 | ℃ | ISO 306/A50 |
| B50 | 67.0 | ℃ | ISO 306 |
| Melting temperature | |||
| DSC | 148 | ℃ | ISO 3146 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 40 µ m, blow molded film | 33 | ASTM D2457 | |
| Haze | |||
| 40 µ m, blow molded film | 19 | % | ISO 14782 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1100 | MPa | ISO 527-2 |
| Bending modulus | 1000 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 84 | ISO 2039-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |