| About |
|---|
| TOTAL POLYSTYRENE 260-25 is an easy flow, high impact polystyrene for injection molding application. 260-25 contains a significant level of recycled polystyrene. This grade is recommended for manufacturing of articles which require good dimensional stability. Applications TV Cover Office Automation Electric and Electronic&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good Dimensional Stability,Good liquidity,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 8.0 | g/10min | ISO 1133 |
| Shrinkage rate | 0.40 to 0.70 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | < 0.10 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 20.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 30 | % | ISO 527-2 |
| Bending modulus | 1800 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 7.5 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 90.0 | ℃ | ISO 306/A50 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Dielectric strength | 160 | kV/mm |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70 | °C | |
| Drying time | 2.0 | hr | |
| Processing (melt) temperature | < 240 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |