| POLYSTYRENE (PS) COMPOUND (CPD) 801 is a high impact brominated flame retardant polystyrene for use in injection moulding and extrusion/thermoforming. PS CPD 801 can be supplied in both natural and coloured forms. Main Characteristics: Excellent UV stability UL94 V0 @ 1.6 mm and UL94 5VB @ 2.5 mm. Application: Covers for electrical equipment. Office automation.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | PS (IRPS) |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High impact resistance,Flame Characteristics,Bromination,V-0,5VB |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | < 1.13 | g/cm³ | ISO 1183 |
| Apparent density | 0.60 | g/cm³ | |
| Melt Flow Rate | |||
| 200℃，5.0kg | 5.0 | g/10min | ISO 1133 |
| Shrinkage rate | 0.40 to 0.70 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | < 0.10 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 527-2 | ||
| yield | 24.0 | MPa | ISO 527-2 |
| fracture | 19.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 40 | % | ISO 527-2 |
| Bending modulus | 2300 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 8.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| B50 | 87.0 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm, all colors | V-0 | UL 94 | |
| 2.50 mm | 5VB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | < 260 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |