TOTAL Polystyrene Crystal 1810

About
POLYSTYRENE CRYSTAL 1810 is a very easy flowing crystal polystyrene designed for the injection moulding industry. The excellent processing characteristics of this grade allows for the production of articles which are very thin and/or have complex flow patterns. In extrusion, POLYSTYRENE CRYSTAL 1810 is used as a high gloss capping layer in co-extrusion. Applications Transparent boxes, office equipment – tape dispensers, pen bodies, masterbatches, capping layer for various articles, internal parts for refrigerators, toys and games.&&

About

POLYSTYRENE CRYSTAL 1810 is a very easy flowing crystal polystyrene designed for the injection moulding industry. The excellent processing characteristics of this grade allows for the production of articles which are very thin and/or have complex flow patterns. In extrusion, POLYSTYRENE CRYSTAL 1810 is used as a high gloss capping layer in co-extrusion. Applications Transparent boxes, office equipment – tape dispensers, pen bodies, masterbatches, capping layer for various articles, internal parts for refrigerators, toys and games.&&

Product Description
Supplier	TOTAL
Generic	PS (GPPS)
Material Status	Commercial: Active
Features	Excellent Processability,Good surface appearance,Good liquidity
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.05	g/cm³	ISO 1183
Apparent density	0.60	g/cm³
Melt Flow Rate
200℃，5.0kg	20	g/10min	ISO 1133
Shrinkage rate	0.40 to 0.70	%
Water absorption rate
Equilibrium, 23 ℃, 50% RH	< 0.10	%	ISO 62

IMPACT	Nominal value	Unit	Test method
Charpy Unnotch Impact strength	8.0	kJ/m²	ISO 179/1eU

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature			ISO 75-2/A
1.8 MPa, unannealed	72.0	℃	ISO 75-2/A
1.8 MPa, annealed	81.0	℃	ISO 75-2/A
Vicat Softening Temp
A50	90.0	℃	ISO 306/A50
B50	85.0	℃	ISO 306
Linear coefficient of thermal expansion
MD	7.1E-5	1/℃

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	> 1.0E+15	ohms	IEC 60093
Dielectric strength	140	kV/mm

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
Level L	70		ISO 2039-2
Tensile modulus	3100	MPa	ISO 527-2
tensile strength
fracture	42.0	MPa	ISO 527-2
Tensile strain
fracture	2.0	%	ISO 527-2
Bending modulus	2900	MPa	ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.