| About |
|---|
| Toyolac® 100 X01 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or Europe. Important attributes of Toyolac® 100 X01 are: Flame Rated RoHS Compliant&& |
| Product Description | |
|---|---|
| Supplier | Toray |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 15 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 26 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 160 | J/m | ASTM D256 |
| -30℃，12.7mm | 140 | J/m | ASTM D256 |
| 0℃，3.2mm | 230 | J/m | ASTM D256 |
| 0℃，12.7mm | 200 | J/m | ASTM D256 |
| 23℃，3.2mm | 310 | J/m | ASTM D256 |
| 23℃，12.7mm | 290 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed | 80.0 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed, 6.4 mm | 85.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 12.7 mm | 91.0 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 7.6E-5 | 1/℃ | ASTM D696 |
| Thermal conductivity coefficient | 0.15 | W/m/K | ASTM C177 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+16 | ohms | ASTM D257 |
| Volume resistivity | |||
| 23℃ | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | 24 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 kHz | 3.10 | ASTM D150 | |
| Dissipation factor | |||
| 1 kHz | 6.5E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 44.0 | MPa | ISO 527-2/50 |
| yield | 41.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 40 | % | ASTM D638 |
| fracture | > 10 | % | ISO 527-2/50 |
| Bending modulus | 1960 | MPa | ASTM D790 |
| bending strength | 63.0 | MPa | ASTM D790 |
| bending strength | 63.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 105 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 0.12 in/min |
| 4. 0.079 in/min |
| 5. 23°C |
| 6. Method A (Short-Time) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |