| About |
|---|
| Toyolac® 855VG20是一种丙烯腈丁二烯苯乙烯(ABS)产品,含有的填充物为20% 玻璃纤维增强材料。 它,在亚太地区、北美洲或欧洲有供货。 特性包括: 阻燃/额定火焰 Flame Retardant&& |
| Product Description | |
|---|---|
| Supplier | Toray |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,5VA |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.34 | g/cm³ | ASTM D792 |
| 23℃ | 1.34 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 240℃，10.0kg | 22 | g/10min | ISO 1133 |
| Shrinkage rate | 0.20 to 0.60 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 7.0 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃，12.7mm | 69 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 100 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 100 | ℃ | ISO 75-2/A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 2.50 mm | 5VA | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 118 | ASTM D785 | |
| R-level | 118 | ISO 2039-2 | |
| tensile strength | |||
| — | 98.0 | MPa | ASTM D638 |
| 23℃ | 104 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2 |
| Bending modulus | |||
| — | 6860 | MPa | ASTM D790 |
| 23℃ | 7200 | MPa | ISO 178 |
| bending strength | |||
| — | 137 | MPa | ASTM D790 |
| 23℃ | 155 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |