| About |
|---|
| Toyolac® PX10-X07 is a Polycarbonate + ABS (PC+ABS) product. It is available in Asia Pacific, Europe, or North America. Typical application: Automotive. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | Toray |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ASTM D792 |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 240℃，10.0kg | 29 | g/10min | ISO 1133 |
| Shrinkage rate | 0.40 to 0.70 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 60 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 120 | J/m | ASTM D256 |
| 23℃，3.2mm | 580 | J/m | ASTM D256 |
| 23℃，12.7mm | 330 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 108 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 101 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 115 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 8.0E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 52.0 | MPa | ASTM D638 |
| Yield, 23 ℃ | 57.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 50 | % | ISO 527-2 |
| fracture | 50 | % | ASTM D638 |
| Bending modulus | 2100 | MPa | ASTM D790 |
| 23℃ | 2180 | MPa | ISO 178 |
| bending strength | 79.0 | MPa | ASTM D790 |
| 23℃ | 84.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 114 | ISO 2039-2 | |
| R-level | 114 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |