| About |
|---|
| TPSiV® 4100-60A Thermoplastic Elastomer is a thermoplastic elastomer with superior compression set and mechanical properties with excellent bonding to Polycarbonate, ABS, and similar polar substrates.&& |
| Product Description | |
|---|---|
| Generic | TPSiV |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Good wear resistance,Soft,High scratch resistance,Agglomerability |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，10.0kg | 10 | g/10min | ISO 1133 |
| Shrinkage rate | 1.0 to 3.0 | % | |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 9.40 | MPa | ISO 37 |
| 100% strain | 2.00 | MPa | ISO 37 |
| Tensile strain | |||
| fracture | 950 | % | ISO 37 |
| tear strength | 47 | kN/m | ISO 34-1 |
| Compression deformation | ISO 815 | ||
| 23℃，22 hr | 15 | % | ISO 815 |
| 70℃，22 hr | 45 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds | 60 | ISO 868 | |
| Bending modulus | 27.3 | MPa | ISO 178 |
| bending strength | 1.50 | MPa | ISO 178 |
| Taber abraser | |||
| 1000 cycles | 51.0 | mg | ASTM D1044 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 65 to 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 165 to 175 | °C | |
| Barrel middle temperature | 170 to 180 | °C | |
| Barrel front temperature | 180 to 195 | °C | |
| Nozzle temperature | 185 to 200 | °C | |
| Processing (melt) temperature | 195 | °C | |
| Mold temperature | 20 to 40 | °C | |
| Injection speed | 中等偏快 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |