| About |
|---|
| TPX™ DX350是一种聚甲基戊烯共聚物（PMP 共聚物）产品,。 它,在非洲和中东或欧洲有供货。 |
| Product Description | |
|---|---|
| Supplier | Mitsui |
| Generic | 聚甲基戊烯共聚物 |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.832 | g/cm³ | |
| Melt Flow Rate | |||
| 260℃，5.0kg | 110 | g/10min | |
| surface tension | 25 | mN/m | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 19 | J/m | |
| Notched impact strength of cantilever beam | 9.0 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 127 | ℃ | ASTM D648 |
| Vicat Softening Temp | 168 | ℃ | |
| Melting peak temperature | 232 | °C |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 87 | ||
| Tensile modulus | 1900 | MPa | |
| Tensile strength (yield) | 29.0 | MPa | |
| Tensile strain | |||
| fracture | 14 | % | |
| Bending modulus | 1500 | MPa | |
| bending strength | 36.0 | MPa |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |