| About |
|---|
| TRANSMARE® 35HGF30-0.001 is a 30% chemically coupled glass fiber reinforced polypropylene homopolymer. It combines good impact properties with a high stiffness, and very good flow properties.&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Renewable resources,Good liquidity,Chemical coupling,Homopolymer |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 15 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 75 | ISO 868 | |
| Tensile modulus | |||
| 4 mm | 6470 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 4 mm | 90.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 4 mm | 3.0 | % | ISO 527-2/50 |
| Bending modulus | 5450 | MPa | ISO 178 |
| bending strength | 125 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40℃ | 7.0 | kJ/m² | ISO 179/1A |
| 23℃ | 9.0 | kJ/m² | ISO 179/1A |
| Charpy Unnotch Impact strength | ISO 179/1U | ||
| -40℃ | 33 | kJ/m² | ISO 179/1U |
| 23℃ | 45 | kJ/m² | ISO 179/1U |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40℃ | 7.0 | kJ/m² | ISO 180-1A |
| 23℃ | 10 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -40℃ | 35 | kJ/m² | ISO 180/1U |
| 23℃ | 44 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 133 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 156 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 162 | ℃ | ISO 306/A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Recommended maximum moisture content | < 0.20 | % | |
| Barrel rear temperature | 170 | °C | |
| Barrel middle temperature | 230 | °C | |
| Barrel front temperature | 240 | °C | |
| Nozzle temperature | 250 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Injection speed | Slow-Moderate | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 3-point |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |