| About |
|---|
| Product Description: TREXPRENE ® A80BU is a heat stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV). This Black compound is intended primarily for underhood applications such as mats, seals, gaskets, air ducts, CVJ boots, covers, grommets or other parts where softness and conformity are needed. This material can be processed using Injection Molding, Extrusion, Blow Molding or other melt processing techniques.&& |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | TPV |
| Material Status | Commercial: Active |
| Features | Soft,Heat Stabilized |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 to 1.00 | g/cm³ | ISO 1183 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 37 | ||
| TD, 100% strain | 4.00 | MPa | ISO 37 |
| MD, 100% strain | 5.70 | MPa | ISO 37 |
| tensile strength | ISO 37 | ||
| fracture | 9.30 | MPa | ISO 37 |
| MD, fracture | 8.30 | MPa | ISO 37 |
| Tensile strain | ISO 37 | ||
| fracture | 750 | % | ISO 37 |
| Flow rate, fracture | 480 | % | ISO 37 |
| tear strength | ISO 34-1 | ||
| TD | 37 | kN/m | ISO 34-1 |
| MD | 38 | kN/m | ISO 34-1 |
| Compression deformation | ASTM D395B | ||
| 70℃，22 hr | 43 | % | ASTM D395B |
| 125℃，70 hr | 57 | % | ASTM D395B |
| Compression deformation | ISO 815 | ||
| 70℃，22 hr | 43 | % | ISO 815 |
| 125℃，70 hr | 57 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw’s A | 80 to 86 | ISO 868 | |
| Shore A, 15 seconds | 77 to 83 | ISO 868 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -59.0 | ℃ | ASTM D746 |
| Brittleness Temperature（Type B） | -59.0 | ℃ | ISO 812 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | ISO 188 | ||
| 135℃，1000 hr | -2.0 | % | ISO 188 |
| 150℃，168 hr | -7.4 | % | ISO 188 |
| Changes in tensile stress during fracture in air | ISO 188 | ||
| 135℃，1000 hr | -12 | % | ISO 188 |
| 150℃，168 hr | -15 | % | ISO 188 |
| Change in Tensile Stress（125℃，70 hr，in IRM 903 Oil） | -37 | % | ISO 1817 |
| Change in Tensile Strain at Break（125℃，70 hr，in IRM 903 Oil） | -57 | % | ISO 1817 |
| Volume change | |||
| 125 ℃, 70 hr, in IRM 903 oil | 78 | % | ISO 1817 |
| Change rate of tear strength | |||
| 70 hrs，in IRM 903 Oil，125℃ | -58 | % | ISO 1817 |
| Change in Tensile Properties | |||
| Stress at 100% Elongation in Air，168 hrs：150℃ | 12 | % | ISO 188 |
| Stress at 100% Elongation in IRM 903 Oil，70 hrs：125℃ | -8.0 | % | ISO 1817 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | 26 | mm/min | ISO 3795 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ozone resistance | |||
| 40℃ | 0 Rating | ISO 1431-1 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type 1, 20 in/min |
| 3. Method Ba, Angle (Unnicked), 20 in/min |
| 4. Type A |
| 5. 100 pphm, Method A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |