| About |
|---|
| Tribocomp® PA66 PA66 LGF30 PTFE18 N6, is a 30% long glass fiber reinforced, high-flow PA66 with a pellet length of 8mm and 18% PTFE having excellent tribological performance. It can easily be processed on most injection molding machines.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High Friction,High liquidity,Low contractility,Good wear resistance,Heat Stabilized |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.53 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.40 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.4 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 10500 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 195 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 8300 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 260 | MPa | ISO 178 |
| friction coefficient | |||
| dynamic | 0.23 | ||
| static state | 0.18 | ||
| Wear factor | 13.0 | ASTM D3702 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 19 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 65 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 255 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 253 | ℃ | ISO 75-2/A |
| Thermal conductivity coefficient | 0.29 | W/m/K | ISO 22007 |
| Linear coefficient of thermal expansion | 2.9E-5 | cm/cm/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 2 mm | 35 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 500 | V | IEC 60112 |
| Surface resistivity | 1.0E+12 | ohms/sq | ASTM D257 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel rear temperature | 270 to 300 | °C | |
| Barrel middle temperature | 270 to 300 | °C | |
| Barrel front temperature | 285 to 300 | °C | |
| Nozzle temperature | 285 to 310 | °C | |
| Processing (melt) temperature | < 300 | °C | |
| Mold temperature | 80 to 140 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |