Tribocomp® PA66 LGF30 TS0 S8

About
Tribocomp® PA66 LGF30 TS0 S8, is a 30% long glass fiber reinforced, black, high-flow PA66 with a pellet length of 8mm and 15% PTFE having excellent tribological performance. It can easily be processed on most injection molding machines.&&

Product Description
Supplier	Solvay
Generic	PA66
Material Status	Commercial: Active
Features	Good Rigidity,High Friction,High liquidity,Low contractility,Good wear resistance,Heat Stabilized
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.50	g/cm³
Shrinkage rate
MD	0.40	%
Water absorption rate
Equilibrium, 23 ℃, 50% RH	1.4	%

MECHANICAL	Nominal value	Unit
Tensile modulus
23℃	10500	MPa
90℃	7100	MPa
120℃	5500	MPa
tensile strength
Fracture, 23 ℃	190	MPa
Fracture, 90 ℃	120	MPa
Fracture, 120 ℃	95.0	MPa
Tensile strain
fracture	3.0	%
Bending modulus
23℃	8300	MPa
bending strength
23℃	260	MPa
friction coefficient
dynamic	0.23
static state	0.18
Wear factor	13.0

IMPACT	Nominal value	Unit
Charpy Notched Impact Strength
23℃	19	kJ/m²
Charpy Unnotch Impact strength
23℃	65	kJ/m²

THERMAL	Nominal value	Unit
Hot deformation temperature
0.45 MPa, unannealed	255	℃
1.8 MPa, unannealed	253	℃
Thermal conductivity coefficient	0.29	W/m/K
Linear coefficient of thermal expansion	2.9E-5	cm/cm/℃

Electrical performance	Nominal value	Unit
Dielectric strength
2 mm	35	kV/mm
Compared to the leakage tracing index	500	V
Surface resistivity	1.0E+12	ohms/sq

Supplementary information	Nominal value	Unit	Test method

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	100	°C
Drying time	4.0	hr
Recommended maximum moisture content	0.10	%
Barrel rear temperature	270 to 300	°C
Barrel middle temperature	270 to 300	°C
Barrel front temperature	285 to 300	°C
Nozzle temperature	285 to 310	°C
Processing (melt) temperature	< 300	°C
Mold temperature	80 to 140	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.