| About |
|---|
| Tribocomp® PA66 LGF35 MoS2 S9 is a 35% long glass fiber reinforced high-flow PA66 with a pellet length of 9mm and MoS2. It can easily be processed on most injection molding machines. |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High liquidity,Low contractility,Good wear resistance,Heat Stabilized |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.44 | g/cm³ | |
| Shrinkage rate | |||
| MD | 0.30 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.4 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 12200 | MPa | |
| 90℃ | 8200 | MPa | |
| 120℃ | 7200 | MPa | |
| tensile strength | |||
| Yield, 23 ℃ | 215 | MPa | |
| Yield, 90 ℃ | 145 | MPa | |
| Yield, 120 ℃ | 125 | MPa | |
| Tensile strain | |||
| fracture | 3.0 | % | |
| Bending modulus | |||
| 23℃ | 11500 | MPa | |
| bending strength | |||
| 23℃ | 340 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 25 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 70 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 255 | ℃ | |
| 1.8 MPa, unannealed | 253 | ℃ | |
| Thermal conductivity coefficient | 0.31 | W/m/K | |
| Linear coefficient of thermal expansion | 2.5 | cm/cm/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 2 mm | 35 | kV/mm | |
| Compared to the leakage tracing index | 500 | V | |
| Surface resistivity | 1.0E+12 | ohms/sq |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Proposed maximum recycled material ratio | 15 | % | |
| Barrel rear temperature | 270 to 300 | °C | |
| Barrel middle temperature | 270 to 300 | °C | |
| Barrel front temperature | 285 to 300 | °C | |
| Nozzle temperature | 285 to 310 | °C | |
| Processing (melt) temperature | < 300 | °C | |
| Mold temperature | 80 to 160 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |