| About |
|---|
| Trilene HY3.8FY is a polypropylene homopolymer for production of stretched tape (yarn or raffia). Also can be use for transparent woven bag which require good clarity, stiffness. This grade uses Unipol® polypropylene technology with latest catalyst technology.&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Low water portability,Homopolymer |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.903 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 3.8 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 40 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 104 | ℃ | ASTM D648 |
| Vicat Softening Temp | 152 | ℃ | ASTM D1525 4 |
| Melting peak temperature | 163 | ℃ | ASTM D3418 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 100 | ASTM D785 | |
| tensile strength | |||
| yield | 34.0 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 13 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 1290 | MPa | ASTM D790-A |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 230 to 250 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.051 in/min |
| 4. Rate B (120°C/h) |
| 5. 10°C/min, 2nd heat |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |