Trilliant™ HC HC6200-5002 XR Grey

About
The Trilliant® specialty compounds offer a complete system of specialty engineered materials, certified processes, services and technical support that enable healthcare OEM’s to get to market ahead of competition. When specified, Trilliant® compound may incorporate agency rated materials that meet USP Class IV, FDA or ISO 10993 testing requirements. This Trilliant® grade is a high density specialty compound featuring a sustainable material solution for radiation shielding and weighting & balancing applications. The composite material offers a high performance thermoplastic-based alternative to lead. This compound has densities similar to traditional metals and provides greater flexibility in design and processing.&&

About

The Trilliant® specialty compounds offer a complete system of specialty engineered materials, certified processes, services and technical support that enable healthcare OEM’s to get to market ahead of competition. When specified, Trilliant® compound may incorporate agency rated materials that meet USP Class IV, FDA or ISO 10993 testing requirements. This Trilliant® grade is a high density specialty compound featuring a sustainable material solution for radiation shielding and weighting & balancing applications. The composite material offers a high performance thermoplastic-based alternative to lead. This compound has densities similar to traditional metals and provides greater flexibility in design and processing.&&

Product Description
Supplier	Polyone
Generic	PA12
Material Status	Commercial: Active
Features	High density,Nontoxicity
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	8.00	g/cm³	ISO 1183
Shrinkage rate	1.0 to 1.5	%	ISO 294-4

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	5000	MPa	ISO 527-1-2
tensile strength
fracture	45.0	MPa	ISO 527-2/50
Tensile strain
fracture	1.0 to 2.0	%	ISO 527-2/50

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength	5.0	kJ/m²	ISO 179
Charpy Unnotch Impact strength	15	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	150	℃	ISO 75-2/B
1.8 MPa, unannealed	110	℃	ISO 75-2/A
Thermal conductivity coefficient	1.5 to 2.0	W/m/K	ASTM E1461

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	< 1.0E+3	ohms	IEC 60093

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	4.0	hr
Processing (melt) temperature	230 to 280	°C
Mold temperature	65 to 100	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.