| About |
|---|
| TRIREX is the registered trademark of polycarbonate resin manufactured by Samyang Corporation. TRIREX polycarbonate resins offer superior mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, electronic, appliance, automotive and optical industries. TRIREX 3020HF is a polycarbonate resin grade which has high low temperature impact strength in combination with superior mechanical and physical property. CHARACTERISTICS Superior low temperature impact resistance Good flow-ability Workable under a wide range of temperatures (-100 ? ~ 135 ?) High electrical performance Good dimensional stability Low moisture absorbency Good weather resistance APPLICATIONS TRIREX 3020HF resin grade is designed for injection molding products. High flow viscosity. Transparent colors only.&& |
| Product Description | |
|---|---|
| Supplier | Samyang |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High Viscosity,Good Dimensional Stability,Good Electrical Properties,Good liquidity,low-temperature impact resistance,Low moisture absorption,V-2 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 23 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.0 mm | 0.50 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.15 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 67.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 130 | % | ASTM D638 |
| Bending modulus | 2250 | MPa | ASTM D790 |
| bending strength | |||
| yield | 93.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 790 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 133 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 5.0E-5 to 7.0E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | 30 | kV/mm | ASTM D149 |
| Arc resistance | 120 | sec | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-2 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 235 to 260 | °C | |
| Barrel middle temperature | 250 to 275 | °C | |
| Barrel front temperature | 265 to 290 | °C | |
| Nozzle temperature | 265 to 300 | °C | |
| Processing (melt) temperature | 265 to 300 | °C | |
| Mold temperature | 65 to 105 | °C | |
| Back pressure | 0.250 to 0.700 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.020 to 0.080 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |