| About |
|---|
| TRISTAR® PC-10FRN is a Polycarbonate (PC) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of TRISTAR® PC-10FRN include electrical/electronic applications and wire & cable. Characteristics include: Flame Rated REACH Compliant RoHS Compliant Flame Retardant Good Mold Release&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good stripping performance,Flame Characteristics |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.23 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 23℃，24hr | 0.18 | % | ASTM D570 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 15 | g/10min | ASTM D1238 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 135 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | 7.02E-5 | cm/cm/℃ | ASTM E831-06 |
| Linear coefficient of thermal expansion | 6.84E-5 | cm/cm/℃ | ASTM E831-06 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dissipation factor | |||
| Arc resistance | 60-120 | sec | ASTM D495 |
| Compared to the leakage tracing index | 250-400 | V | ASTM D3638 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 | |
| 2.50 mm | 5VA | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Extreme oxygen index | 37.6 | % | ASTM D2863 |
| Igniting temperature of the hot wire | 775 | ℃ | IEC 60695-2-12 |
| Relative temperature of heating wire | 775 | ℃ | IEC 60695-2-13 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 587 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 120 | R 级 | ASTM D785 |
| tensile strength | |||
| Yield, 23 ℃, 3.17 mm | 62.1 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, 3.17 mm | 75 | % | ASTM D638 |
| bending strength | |||
| 3.17mm，屈服，23°C | 89.6 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃，3.17 mm | 2210 | MPa | ASTM D790 |
| Tensile impact strength | 443 | kJ/m² | ASTM D1822 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 4 | Hr | |
| Injection temperature | |||
| Rear barrel temperature | 254-274 | °C | |
| Central temperature of the barrel | 266-277 | °C | |
| Barrel front temperature | 277-293 | °C | |
| Die temperature | 271-293 | °C | |
| Mold temperature | 71.1-93.3 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |