| About |
|---|
| TRISTAR® PC-10GFR是一种聚碳酸酯（PC）产品,含有的填充物为10% 玻璃纤维增强材料。 它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 TRISTAR® PC-10GFR的应用领域包括电气/电子应用 和 电线电缆。 特性包括: 阻燃/额定火焰 符合 REACH 标准 通过 ROHS 认证 脱模剂 优良的脱模剂&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good stripping performance,V-0,5VA |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.20 to 0.40 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.12 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 110 | J/m | ASTM D256 |
| Tensile impact strength | |||
| 3.17 mm | 53.3 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 138 | ℃ | ASTM D648 |
| Relative temperature index | 80.0 to 125 | ℃ | UL 746 |
| Electrical performance | 80.0 to 125 | ℃ | UL 746 |
| Impact mechanical performance | 80.0 to 115 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | ASTM D257 | ||
| — | 3.0E+15 | ohms·cm | ASTM D257 |
| — | 6.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 3 mm | 19 | kV/mm | ASTM D149 |
| Arc resistance | 0.00 to 120 | sec | ASTM D495 |
| Arc resistance | PLC 7 PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | 100 to 250 | V | UL 746 |
| Compared to the leakage tracing index | PLC 4 PLC 3 | UL 746 | |
| High Arc Burning Index (HAI) | > 120 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | 80.0 to 150 | mm/min | UL 746 |
| HVTR | PLC 3 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 2 PLC 1 | UL 746 | |
| HWI | 30 to 120 | sec | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| 2.40 mm | 5VA | UL 94 | |
| Glowing wire flammability index | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | 875 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 37 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ASTM D785 | |
| tensile strength | |||
| Yield, 3.17 mm | 62.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.17 mm | 15 | % | ASTM D638 |
| Bending modulus | |||
| 3.17 mm | 3100 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 3.17 mm | 96.5 | MPa | ASTM D790 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |