| TRISTAR® PC-10GFR-(V) is a Polycarbonate (PC) product filled with 10% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of TRISTAR® PC-10GFR-(V) include outdoor applications, electrical/electronic applications and wire & cable. Characteristics include: Flame Rated REACH Compliant RoHS Compliant Good Mold Release Mold Release Agent&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good stripping performance,V-0,5VA |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.20 to 0.40 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.12 | % | ASTM D570 |
| Weathering resistance | UL 746C | ||
| White | f2 | UL 746C | |
| — | f1 | UL 746C | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 110 | J/m | ASTM D256 |
| Tensile impact strength | |||
| 3.17 mm | 53.3 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 138 | ℃ | ASTM D648 |
| Relative temperature index | 80.0 to 125 | ℃ | UL 746 |
| Electrical performance | 80.0 to 125 | ℃ | UL 746 |
| Impact mechanical performance | 80.0 to 115 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | ASTM D257 | ||
| — | 3.0E+15 | ohms·cm | ASTM D257 |
| — | 6.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 3 mm | 19 | kV/mm | ASTM D149 |
| Arc resistance | 0.00 to 120 | sec | ASTM D495 |
| Arc resistance | PLC 7 PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | 100 to 250 | V | UL 746 |
| Compared to the leakage tracing index | PLC 4 PLC 3 | UL 746 | |
| High Arc Burning Index (HAI) | > 120 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | 80.0 to 150 | mm/min | UL 746 |
| HVTR | PLC 3 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 2 PLC 1 | UL 746 | |
| HWI | 30 to 120 | sec | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| 2.40 mm | 5VA | UL 94 | |
| Glowing wire flammability index | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | 875 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 37 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ASTM D785 | |
| tensile strength | |||
| Yield, 3.17 mm | 62.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.17 mm | 15 | % | ASTM D638 |
| Bending modulus | |||
| 3.17 mm | 3100 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 3.17 mm | 96.5 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 40 hours at 23°C, 50% RH |
| 3. 96 hours at 90°C, 50% RH |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |