| Eastman Tritan™ FX200 is an amorphous copolyester that combines excellent clarity and toughness with outstanding heat and chemical resistance. Films manufactured from this new-generation copolyester can be thermoformed without pre-drying and with a wide processing window that allows for product designs that reflect intricate detail. Eastman Tritan™ FX200 copolyester may be used in repeated use food contact articles under United States Food and Drug Administration (FDA) regulations.&& |
| Product Description | |
|---|---|
| Supplier | Eastman |
| Generic | PCTG |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good flexibility,Food contact compliance,High Heat Resistance,No BPA,Solvent resistance,Amorphous |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 23℃，24hr，0.254 mm | 0.50 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Taber abraser | |||
| 23℃，250.0 µm | 20Haze | % | ASTM D1044 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 250 | µm | |
| Membrane puncture strength | |||
| 250 µm | 4.50 | J | ASTM D3763 |
| Secant modulus | |||
| TD，250 µm | 1400 | MPa | ASTM D882 |
| MD，250 µm | 1500 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture, 250 µ m | 42.0 | MPa | ASTM D882 |
| TD, yield, 250 µ m | 41.0 | MPa | ASTM D882 |
| MD, fracture, 250 µ m | 57.0 | MPa | ASTM D882 |
| MD, yield, 250 µ m | 43.0 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 250 µ m | 120 | % | ASTM D882 |
| TD, yield, 250 µ m | 8.0 | % | ASTM D882 |
| MD, fracture, 250 µ m | 110 | % | ASTM D882 |
| MD, yield, 250 µ m | 8.0 | % | ASTM D882 |
| Drop hammer impact | ASTM D1709A | ||
| -30℃，250 µm | 830 | g | ASTM D1709-A |
| -18℃，250 µm | 830 | g | ASTM D1709-A |
| 23℃，250 µm | 830 | g | ASTM D1709-A |
| Pant tear resistance | ISO 6383-1 | ||
| MD：250 µm | 10.0 | N/mm | ISO 6383-1 |
| TD：250 µm | 9.00 | N/mm | ISO 6383-1 |
| Oxygen permeability | |||
| 23℃，250 µm，50% RH | 44 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water vapor transmittance | ASTM F1249 | ||
| 23℃，100% RH，250 µm | 4.0 | g/m²/24 hr | ASTM F1249 |
| 38℃，100% RH，250 µm | 10 | g/m²/24 hr | ASTM F1249 |
| Carbon dioxide permeability | |||
| 23℃，254.0 µm | 210 | cm³·mm/m²/atm/24 hr | ASTM D1434 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：23℃，250.0 µm | 4 | N | ASTM D1922 |
| TD：23℃，250.0 µm | 4 | N | ASTM D1922 |
| PPT tear resistance | ASTM D2582 | ||
| MD：23℃，250.0 µm | 40 | N | ASTM D2582 |
| TD：23℃，250.0 µm | 40 | N | ASTM D2582 |
| Tear resistant vine ductility | ASTM D1938 | ||
| MD：23℃，250.0 µm | 310 | gf | ASTM D1938 |
| TD：23℃，250.0 µm | 200 | gf | ASTM D1938 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | ASTM D1938 | ||
| cracking | 9.0 | kN/m | ASTM D1938 |
| cracking | 10 | kN/m | ASTM D1938 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 119 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD：23℃ | 8.0E-5 | 1/℃ | ASTM D696 |
| specific heat | DSC | ||
| 60℃ | 1700 | J/kg/℃ | DSC |
| 100℃ | 1900 | J/kg/℃ | DSC |
| 150℃ | 2300 | J/kg/℃ | DSC |
| 200℃ | 2400 | J/kg/℃ | DSC |
| 250℃ | 2600 | J/kg/℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60°，250 µm | 158 | ASTM D2457 | |
| Refractive index | 1.540 | ASTM D542 | |
| Transmittance | |||
| 250 µm | 93.0 | % | ASTM D1003 |
| Haze | |||
| 250 µm | 0.80 | % | ASTM D1003 |
| Yellowness index | |||
| 250 mm | 0.50 | YI | ASTM D1925 |
| UV transmittance (250.0 µ m) | 89 | % |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface energy | ASTM D5946 | ||
| Dispersive：23℃，250.0 µm | 39 | dyne/cm | ASTM D5946 |
| Polar：23℃，250.0 µm | 8 | dyne/cm | ASTM D5946 |
| Total：23℃，250.0 µm | 47 | dyne/cm | ASTM D5946 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. average at 25 cycles |
| 3. Dynatup, Total Energy |
| 4. 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop |
| 5. 7.9 in/min |
| 6. TD, 250 µm, 254 mm/min |
| 7. MD, 250 µm, 254 mm/min |
| 8. Transmission at 380 nm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |