| About |
|---|
| Eastman Tritan copolyester MP150 is a high flow grade of Eastman Tritan. Eastman Tritan copolyester MP150 has viscosity reductions of 40-50% relative to Eastman Tritan copolyester MP100. It is intended for use in extrusion coating processes or where high melt flow rate is desirable. Other outstanding features include good toughness, hydrolytic stability, and heat and chemical resistance. Eastman Tritan copolyester MP150 may be used in food contact applications with restrictions and is compliant with applicable and select sections of USP 35 <661>, ISO10993, and ISO11607.&& |
| Product Description | |
|---|---|
| Supplier | Eastman |
| Generic | PCTG |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good flexibility,High liquidity,Hydrolysis stability,Food contact compliance,High Heat Resistance,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D1505 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 130 | µm | |
| Elastic modulus | |||
| MD, cast thin film | 979 | MPa | ASTM D882 |
| tensile strength | |||
| fracture | 52.0 | MPa | ASTM D638 |
| yield | 43.0 | MPa | ASTM D638 |
| MD, fracture, blow molded film | 56.5 | MPa | ASTM D882 |
| Tensile strain | |||
| fracture | 210 | % | ASTM D638 |
| yield | 7.0 | % | ASTM D638 |
| MD, fracture, extruded film | 220 | % | ASTM D882 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | No Break | ASTM D4812 | |
| 23℃ | 860 | J/m | ASTM D256 |
| Drop hammer impact | |||
| 0.127 mm, cast thin film | 3.50 | J | ASTM D5420 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 81.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 94.0 | ℃ | ASTM D648 |
| Glass transition temperature | 110 | ℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| total | 91.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1580 | MPa | ASTM D638 |
| Bending modulus | 1580 | MPa | ASTM D790 |
| bending strength | |||
| yield | 64.0 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 111 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 88 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Processing (melt) temperature | 260 to 282 | °C | |
| Mold temperature | 38 to 66 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |