| About |
|---|
| Eastman Tritan MP200 is an amorphous copolyester that combines excellent clarity and toughness with outstanding heat and chemical resistance. Film and sheet manufactured from this new-generation copolyester can be thermoformed with a wide processing window that allows for product designs that reflect intricate detail. Eastman Tritan MP200 copolyester is suitable for use with most forms of sterilization including radiation and ethylene oxide. It is NOT suitable for autoclave/steam sterilization. Eastman Tritan MP200 copolyester has been formulated for use in medical film, sheet, and packaging applications.&& |
| Product Description | |
|---|---|
| Supplier | Eastman |
| Generic | PCTG |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good flexibility,Good surface appearance,Steam sterilized,High pressure disinfection,High Heat Resistance,Radiation disinfection,Solvent resistance,Ethylene oxide disinfection,Amorphous |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D1505 |
| Water absorption rate | |||
| 24hr | 0.50 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Wear resistance | |||
| 23℃ | 20% Haze | ASTM D1044 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 250 | µm | ASTM D374 |
| Elastic modulus | |||
| TD，250 µm | 1400 | MPa | ASTM D882 |
| MD，250 µm | 1500 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture, 250 µ m | 42.0 | MPa | ASTM D882 |
| TD, yield, 250 µ m | 41.0 | MPa | ASTM D882 |
| MD, fracture, 250 µ m | 57.0 | MPa | ASTM D882 |
| MD, yield, 250 µ m | 43.0 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 250 µ m | 120 | % | ASTM D882 |
| TD, yield, 250 µ m | 8.0 | % | ASTM D882 |
| MD, fracture, 250 µ m | 110 | % | ASTM D882 |
| MD, yield, 250 µ m | 8.0 | % | ASTM D882 |
| Drop hammer impact | ASTM D1709A | ||
| -30℃，250 µm | 850 | g | ASTM D1709-A |
| -18℃，250 µm | 830 | g | ASTM D1709-A |
| 23℃，250 µm | 830 | g | ASTM D1709-A |
| Elmandorf tear strength | |||
| MD，250 µm | 380 | g | ASTM D1922 |
| tear strength | |||
| TD，250 µm | 430 | g | ASTM D1922 |
| Pant tear resistance | ISO 6383-1 | ||
| MD：250 µm | 10.0 | N/mm | ISO 6383-1 |
| TD：250 µm | 9.00 | N/mm | ISO 6383-1 |
| Oxygen transfer rate | |||
| 23℃，250 µm | 44 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water vapor transmittance | ASTM F1249 | ||
| 23℃，100% RH，250 µm | 4.0 | g/m²/24 hr | ASTM F1249 |
| 38℃，100% RH，250 µm | 10 | g/m²/24 hr | ASTM F1249 |
| Carbon dioxide permeability | |||
| 23℃，254.0 µm | 210 | cm³·mm/m²/atm/24 hr | ASTM D1434 |
| PPT tear resistance | ASTM D2582 | ||
| MD：23℃，254.0 µm | 40 | N | ASTM D2582 |
| TD：23℃，254.0 µm | 40 | N | ASTM D2582 |
| Tear resistant vine ductility | ASTM D1938 | ||
| MD，Split Tear Method：23℃，254.0 µm | 310 | gf | ASTM D1938 |
| TD，Split Tear Method：23℃，254.0 µm | 200 | gf | ASTM D1938 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Dart impact equipped with measuring instruments | |||
| 23℃，0.254 mm，Total Energy | 4.50 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 119 | ℃ | DSC |
| Linear coefficient of thermal expansion | |||
| MD：23℃ | 8.0E-5 | 1/℃ | ASTM D696 |
| specific heat | DSC | ||
| 60℃ | 1700 | J/kg/℃ | DSC |
| 100℃ | 1900 | J/kg/℃ | DSC |
| 150℃ | 2300 | J/kg/℃ | DSC |
| 200℃ | 2400 | J/kg/℃ | DSC |
| 250℃ | 2600 | J/kg/℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60°，254 µm | 158 | ASTM D2457 | |
| Refractive index | 1.540 | ASTM D542 | |
| Transmittance | |||
| Total，254 µm | 93.0 | % | ASTM D1003 |
| Haze | |||
| 254 µm | 0.80 | % | ASTM D1003 |
| Yellowness index | |||
| 0.254 mm | 0.50 | YI | ASTM D1925 |
| UV transmittance | 89 | % |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface energy | ASTM D5946 | ||
| Dispersive：23℃ | 39 | dyne/cm | ASTM D5946 |
| Polar：23℃ | 8 | dyne/cm | ASTM D5946 |
| Total：23℃ | 47 | dyne/cm | ASTM D5946 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 25 cycles |
| 3. 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop |
| 4. 7.9 in/min |
| 5. UV/Vis Spectro, 380 nm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |