| About |
|---|
| Eastman Tritan™ Copolyester MX710 is an amorphous product with excellent appearance and clarity. Eastman Tritan™ Copolyester MX710 has many outstanding features that include excellent toughness, hydrolytic stability, heat resistance, and chemical resistance. Eastman Tritan™ Copolyester MX710 has been formulated for medical devices.&& |
| Product Description | |
|---|---|
| Supplier | Eastman |
| Generic | PCTG |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,Good flexibility,Good surface appearance,High impact resistance,Hydrolysis stability,Quick molding cycle,Good color stability,High Heat Resistance,Radiation disinfection,Solvent resistance,Ethylene oxide disinfection,Amorphous |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -40℃ | 110 | J/m | ASTM D256 |
| 23℃ | 980 | J/m | ASTM D256 |
| -40℃ | 20 | kJ/m² | ISO 180 |
| 23℃ | 93 | kJ/m² | ISO 180 |
| Notched impact strength of cantilever beam | ASTM D4812 | ||
| -40℃ | 无断裂 | ASTM D4812 | |
| 23℃ | 无断裂 | ASTM D4812 | |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -40℃，Energy at Peak Load | 66.0 | J | ASTM D3763 |
| 23℃，Energy at Peak Load | 61.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 99.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 85.0 | ℃ | ASTM D648 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| total | 90.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 112 | ASTM D785 | |
| Tensile modulus | |||
| 23℃ | 1550 | MPa | ASTM D638 , ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 43.0 | MPa | ASTM D638 , ISO 527-2 |
| Fracture, 23 ℃ | 53.0 | MPa | ASTM D638 |
| Fracture, 23 ℃ | 58.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 23 ℃ | 6.0 | % | ASTM D638 |
| Yield, 23 ℃ | 7.0 | % | ISO 527-2 |
| Fracture, 23 ℃ | 210 | % | ASTM D638 |
| Fracture, 23 ℃ | 190 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 1550 | MPa | ASTM D790 |
| 23℃ | 1500 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 59.0 | MPa | ISO 178 |
| Yield, 23 ℃ | 62.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 88 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Processing (melt) temperature | 260 to 282 | °C | |
| Mold temperature | 38 to 66 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |