| About |
|---|
| Eastman Tritan™ copolyester TX1501HF is a high flow grade of Eastman Tritan™. Eastman Tritan™ copolyester TX1501HF has viscosity reductions of 40-50% relative to Eastman Tritan™ copolyester TX1001. Eastman Tritan™ copolyester TX1501HF contains a mold release derived from vegetable based sources. Other outstanding features include good toughness, hydrolytic stability, and heat and chemical resistance. Eastman Tritan™ copolyester TX1501HF may be used in repeated use food contact articles under United States Food and Drug Administration (FDA) regulations. Eastman Tritan™ copolyester TX1501HF is certified to NSF/ANSI Standard 51 for Food Equipment Materials and is also certified to NSF/ANSI Standard 61 – Drinking Water System Components-Health Effects.&& |
| Product Description | |
|---|---|
| Supplier | Eastman |
| Generic | PCTG |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,Good flexibility,High impact resistance,High liquidity,Hydrolysis stability,Low Viscosity,Quick molding cycle,Good stripping performance,Food contact compliance,High Heat Resistance,Durability,Solvent resistance,Amorphous |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180 | ||
| 23℃ | 860 | J/m | ASTM D256 |
| 23℃ | No Break | ASTM D4812 | |
| -40℃ | 11 | kJ/m² | ISO 180 |
| 23℃ | 83 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 81.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 94.0 | ℃ | ASTM D648 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| total | 91.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 1600 | MPa | ISO 527-2 |
| 23℃ | 1580 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 23 ℃ | 52.0 | MPa | ASTM D638 |
| Fracture, 23 ℃ | 49.0 | MPa | ISO 527-2 |
| Yield, 23 ℃ | 44.0 | MPa | ISO 527-2 |
| Yield, 23 ℃ | 43.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 210 | % | ASTM D638 |
| Fracture, 23 ℃ | 150 | % | ISO 527-2 |
| Yield, 23 ℃ | 7.0 | % | ISO 527-2 |
| Yield, 23 ℃ | 7.0 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 1580 | MPa | ASTM D790 |
| 23℃ | 1500 | MPa | ISO 178 |
| bending strength | |||
| Yield, 23 ℃ | 64.0 | MPa | ASTM D790 |
| 23℃ | 60.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 111 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 88 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Processing (melt) temperature | 260 to 282 | °C | |
| Mold temperature | 38 to 66 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |